How to ensure the quality of baby silicone products?

With the advancement of technology and the rapid development of the economy, in recent years, silicone materials have been widely used in various industries, especially in the application of maternal and child products, replacing plastic and glass materials. It is healthy, environmentally friendly, non-toxic, and odorless. Food grade materials can be used for baby bottles, dental implants, toys, etc. Medical grade silicone material can be implanted into the human body and is biocompatible. The high-quality characteristics of silicone make it suitable for all aspects of our lives.

1. Silicone is a material with a feeling similar to human skin, and a good baby silicone product should first have a good hand feel. Here we take a silicone baby bottle as an example. When feeding a baby, the baby's cute little hands hold the bottle, and the touch of the bottle on the baby is like a mother's loving touch. After the baby is born and leaves their original growth environment, the baby lacks a sense of security. Some babies often cry and make us feel helpless as new parents. However, silicone baby products that feel like a mother's touch give babies this sense of security. Therefore, good baby silicone products are beneficial for the development of babies in all aspects. This is also incomparable to other materials of milk bottles.

2. Silicone milk bottles should be easy to use. Disassembly and assembly should be convenient, universal, and interchangeable with other pacifiers and baby bottles. Some silicone baby bottles are now impractical to disassemble and assemble. Install card slots and set card patterns between the silicone and the plastic cover in the middle. The most important aspect of a bottle is its practicality and convenience.

Performance and material of baby silicone products
1. If the surface of real silicone rubber is not specially treated, it will feel relatively smooth to the touch because there is a layer of oily substance on the surface layer
2. Fake silicone rubber is prone to deformation, while real silicone rubber has good rebound and is not easily deformed after pulling and rebounding.
3. Good silicone has no odor and does not soften or change color when exposed to heat.
4. Cut off a little bit of silicone and burn it with fire. The edge of the fake silicone rubber wristband is black after being burned. The fake silicone rubber burns with an open flame, producing black smoke and a foul odor. But for real silicone, regardless of the color of the silicone, the burning edge is white, and the burning residue is powder. And the real silicone rubber wristband burns like carbon, with even flames. White smoke, odorless.
5. Look at the resilience of silicone products, high-quality silicone products have good resilience. Silicone material itself has good wear resistance, therefore, the surface of silicone products has the ability to resist wear and tear. Generally speaking, high-quality silicone products will not erase surface text, color, etc. due to external factors. On the contrary, the text, characters, and logos on the surface of inferior silicone products are more likely to fall off. High quality silicone products have a bright color, and after special processing, the surface is non sticky, odorless, soft, and has a good hand feel.
6. Silicone products have high tear resistance, long service life, and are not easily affected by external environmental interference. Generally speaking, high-quality silicone products are less prone to cracking during the tearing process, while low-quality silicone products are more prone to cracking. When subjected to force, low-quality silicone products will quickly expand and crack from the crack.
7. When silicone products are subjected to alternating stress (or strain) effects, the phenomenon of changes in the structure and function of the data is called fatigue. The scene of silicone product damage caused by the process of fatigue is called fatigue damage. So fatigue resistance is also one of the ways to distinguish the quality of silicone products.